Mechanical Welded Titanium Tubing Seamless Grade 2 UNS R50400 ASME SB337

Moderate Strength Titanium

Excellent Cold Formability

Excellent Weldability

Excellent Resistance to High Oxidation

Applications:

Bellows, aircraft structural, honeycomb, gaskets, aircraft skin, heat exchanger parts.

Description:

Commercially Pure Grade 2 is slightly stronger than Grade 1 but equally corrosion resistant against most applications. Best strength to weight ratio of any corrosion resistant material. This grade is one of the most common Titanium Grades and is used for Heat exchangers, condenser tubing and bleaching plants in paper industry, offshore oil installation water pipe lines. Can be used for parts requiring strength up to 400°F and oxidation resistance to 600°F.

Chemistry Typical:

Titanium: Balance

Iron: 0.30 max

Oxygen: 0.25 max

Carbon: 0.10 max

Nitrogen: 0.03 max

Hydrogen: 0.015 max

Residuals each 0.10 max, total 0.40 max

Physical Properties:

Density, 0.163 lbs/in³ , 4.51 g/cm³

Mean Coefficient of Thermal Expansion, in/in/°F (mm/m/°C):

70- 212°F (20- 100°C): 4.78 x 10^-6 (8.6)

Thermal Conductivity: BTU-in/h-ft-°F (W/m-°K):

At 70°F (21°C): 114(16.4)

Modulus of Elasticity, ksi (MPa)

15.2 x 10³(105 x 10³) in tension

Melting Point : 3040°F (1670°C)

Properties: Annealed

Ultimate Tensile Strength: 50 KSI min (345 MPa min)

Yield Strength (0.2% offset): 40-65 KSI (276-448 MPa )

Elongation: 20% min

Properties: Tempered

Titanium Grade 2 can be cold rolled to various tempers. Contact Ulbrich Technical Service for additional information.