S30400 22mm stainless steel tube Corrosion Resistance Excellent Weldability Tubing
300 series grade stainless steel is manufactured into a range of products including steel tubes,steel pipes and various other products. Both 304 and 316 steel tubes are nickel-based alloys that are easy to maintain, resist corrosion and maintain strength and durability at high temperatures. Determining which grade of steel is best for your application depends on the intended application as well as environmental factors such as temperature or exposure to chloride.
Description:
Austenitic 304/4301 welded precision stainless steel tubing has excellent weldability and is suitable for the full range of conventional welding methods (like MMA, MIG, MAG, TIG, SAW, LBW, or RSW), except gas welding.
304/4301 have about 50% higher thermal expansion and lower heat conductivity compared to carbon steels. This means that larger deformation and higher shrinkage stresses may result from welding.
In thin sections, autogenous welding may be used. In thicker section, the low-carbon grade 4307 is preferred, and to ensure that the weld metal properties (e.g. strength, corrosion resistance) are equivalent to those of the parent metal, matching or slightly over-alloyed fillers should preferably be used. Recommended filler metal is 19 9 L.
Post-weld heat treatment is generally not required. In special cases where there is high risk of stress corrosion cracking or fatigue, stress relief treatment may be considered.
In order to fully restore the corrosion resistance of the weld seam, the weld discoloration should be removed by pickling and passivation.
| Item Code: | SPW-EN-1.4301 |
| Tube OD.: | 10MM |
| Wall: | 1.0MM |
| Length: | 6000MM |
| Material: | EN 1.4301, ASTM TYPE 304 / UNS S30400 |
| Standard: | EN10217-7 / ASTM A249 / ASME SA249 |
| Finish: | BA / Bright Annealed. |
| Type: | Welded |
| Certification: | ISO9001:2015 |
| Mill Test Certificate: | EN10204 3.1 |
| Packing: | Sleeved, Wooden Boxed |
1.4301 Stainless Steel / Spec: EN 10088-3:2005
| Chemical Element | % ( Weight ) |
| Carbon (C) | 0.0 - 0.07 |
| Chromium (Cr) | 17.50 - 19.50 |
| Manganese (Mn) | 0.0 - 2.00 |
| Silicon (Si) | 0.0 - 1.00 |
| Phosphorous (P) | 0.0 - 0.05 |
| Sulphur (S) | 0.0 - 0.03 |
| Nickel (Ni) | 8.00 - 10.50 |
| Nitrogen (N) | 0.0 - 0.11 |
| Iron (Fe) | Balance |
| Mechanical Property | Value |
| Proof Stress | 190 Min MPa |
| Tensile Strength | 500 to 700 MPa |
| Elongation A50 mm | 45 Min % |
| Hardness Brinell | 215 Max HB |
Available Tube Product Forms:
Straight.
Coiled.
Seam welded and cold redrawn.
Seam welded, cold redrawn and annealed.
Quality Assurance:
Spezilla's EN 1.4301, ASTM TYPE 304 / UNS S30400 welded precision stainless steel tubes are produced acc. to the following process and inspection to assure our quality:
1. Chemical Composition Analysis Test With 100% PMI.
2. Solution Annealing / Bright Annealed.
3. 100% Hydrostatic Test and 100% Eddy Current Test
4. Mechanical Tests includes Tension Test, Flattening Test, Flaring Test, Hardness Test.
5. Impact Test subject to Standard request.
6. Grain Size Test and Intergranular Corrosion Test.
7. Visual Test and Endoscope Test for Surface Quality Test
Typical Applications:
304/4301 welded precision stainless steel tubing can be used for indoor and outdoor applications in rural areas and urban environments where chloride contamination is low. The best material performance is usually reached with the help of adequate design, correct post-weld treatment, and regular cleaning during use (if applicable).
Typical Manufacturing Specifications:
ASTM A249
EN10217-7
EN10296-2
Also individual customer specifications.